| Type: | Roll |
|---|---|
| Temper: | Half Hard |
| Treatment: | Coated |
| Surface State: | Double Light Aluminum Foil |
| Rolling Characteristics: | Rolling |
| Usage: | Electric |
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 1.high tensile strength
2.strong corrosion resistance
3.MOQ:10Sq.m
Specification of Al plastic film for lithium battery
|
Consist |
D-EL40H |
||
|
ON25 |
|||
|
DL4 |
|||
|
AL40 |
|||
|
Improved PPa15 |
|||
|
Improved PP30 |
|||
|
Acid modified resin combination, waterproof and acid attacks (Thickness 114µm) |
|||
|
Thickness |
µm |
Designed |
114 |
|
Steam Barrier Property 60°C90%RH 336H |
PPm |
Sealing Pressure 1.0MPa |
50↓ |
|
Initial strength of laminated layers(AL/PPa) |
N/15mm |
|
11~12 |
|
Initial sealing strength |
N/15mm |
Sealing Pressure 0.5MPa |
70~80 |
|
190°C 3seconds |
Sealing Pressure 1.0MPa |
85↑ |
|
|
The electrolyte resistance(Test for sealing into film strength) |
N/15mm |
|
4.0↑ |
|
60°C 14days |
|||
|
Electrolyte resistance(Test for sealing into film strength) |
N/15mm |
Sealing Pressure 0.5MPa |
40~50 |
|
60°C 14days |
Sealing Pressure 1.0MPa |
50~60 |
|
|
Sealing strength for electrolyte |
N/15mm |
Sealing face pressure 0.5MPa |
80~90 |
|
190°C 3seconds |
Sealing face pressure 1.0MPa |
80~90 |
|
|
Punch forming depth |
mm |
Control drape pressure 0.17MPa (Size:80*120mm) |
5.0↑ |
We could supply one stop solution ( turn key project) for lithium ion battery production line.
1.Full set of lithium battery materials,including :
LiMn2O4,LTO,LiNiMnCoO2(NMC),LiCoO2,Graphite(MCMB)and other cathode&anode batterymaterials;Aluminum foil,copper foils,battery separator,etc.
2.Full set of lithium battery equipments,for example:
mixing machine --coating machine--oven--rolling machine--welding machine--slitting / cutiing machine --winding machine--sealed machine,etc.
3.Full set of lithium battery technology.
we can design the laboratory and production line,according to customer's request.